ERCuAl-A2铝青铜焊丝 HSCuA2铜焊丝HS214

牌 号	主要成份(%)	特性和用途	相当AWS
黄铜焊丝 GMT-CU	Sn Cu Rem	机械性能好，耐磨性好，流动性非常优秀，适合无温冷焊。	ERCuSn-D
紫磷铜焊丝S201	P0.5 Cu Rem.	机械性能好，抗裂性好。紫铜气焊及氩弧焊用	ERCu
硅青铜焊丝S211	Si3 Mn1 Cu Rem.	机械性能好，铜合金氩弧焊及钢的MIG钎焊用	ERCuSi-Al
锡青铜焊丝S212	Sn5 Cu Rem.	耐磨性好。铜合金氩弧焊及钢的堆焊用	ERCuSn-A
锡青铜焊丝S213	Sn8 Cu Rem.	耐磨性好。铜合金氩弧焊及钢的堆焊用	ERCuSn-C
铝青铜焊丝A1S214	Al7.5 Cu Rem.	耐磨、耐蚀。铜合金氩弧焊及钢的堆焊用	ERCuAl-A1
铝青铜焊丝A2S215	Al9 Cu Rem.	耐磨、耐蚀。铜合金氩弧焊及钢的堆焊用	ERCuAl-A2
铝青铜焊丝(A3)	A1 10.5 Cu Rem.	耐磨、耐蚀。铜合金氩弧焊及钢的堆焊用。	ERCuA1-A3
锡黄铜焊丝S221	Cu60 Sn1 Si0.3 Zn Rem.	熔点约890℃。黄铜气焊及碳弧焊用，也可钎焊铜、钢、铸铁
铁黄铜焊丝S222	Cu58 Sn0.9 Si0.1 Fe0.8 Zn Rem.	熔点约880℃。黄铜气焊及碳弧焊用，也可钎焊铜、钢、铸铁	RBCuZn-C
镍铝青铜焊丝-1	Al8 Ni2 Cu Rem	熔点约1038℃-1054℃。耐磨耐蚀，铜合金氩弧焊及钢的钎焊。
镍铝青铜焊丝-2	Al8 Ni6 Cu Rem	熔点约1038℃-1054℃。耐磨耐蚀，铜合金氩弧焊及钢的钎焊。	ERCuNiAl
锌白铜焊丝S225	Cu48 Ni10 Zn Rem.	熔点约935℃。高强度,钎焊钢、镍及硬质合金用	RBCuZn-D2
S225F	Cu48 Ni10 Zn Rem.	外涂焊剂的S225焊丝	RBCuZn-D
S226	Cu60 Sn0.3 Si0.2 Zn Rem.	熔点约900℃。黄铜气焊用，也可钎焊铜、钢、铸铁
S227	Cu58 Sn0.9 Ni0.5 Si0.1 Fe0.8 Zn Rem.	熔点880℃。黄铜气焊及碳弧焊用，也可钎焊铜、钢、铸铁	RBCuZn-B
S229	Cu55 Ni6 Mn4 Zn余量	熔点约920℃。高强度,钎焊钢、镍及硬质合金用

HB-YD601(Z)	3～5	1.4～1.6	0.6～1.0	28～30	?0?2	?0?2	?0?2	HRC ：59～61	用于磨煤辊、磨盘的修复和再制造，以及输送带、料斗、挖掘机、铲齿、筑路机、采石场设备、混料机和鼓风机叶片等堆焊。
HB-YD605(Z)	3～5	1.4～1.6	0.6～1.0	28～30	?0?2	?0?2	B：1～2	HRC ：63～65	用于磨煤辊、磨盘的修复和再制造，以及输送带、料斗、挖掘机、铲齿、筑路机、采石场设备、混料机和鼓风机叶片等堆焊。
HB-YD611(M)	3～5	1.4～1.6	0.6～1.0	28～30	?0?2	?0?2	?0?2	HRC ：59～61	用于磨煤辊、磨盘的修复和再制造，以及输送带、料斗、挖掘机、铲齿、筑路机、采石场设备、混料机和鼓风机叶片等堆焊

HB-YD467耐磨药芯焊丝

说明： YD132-1是CO2气体保护的CrMo型堆焊药芯焊丝。堆焊时电弧稳定，脱渣容易。
用途：适用于耐冲击，中度磨损的情况。用于低碳钢、中碳钢或低合金钢机件表面的修补，如矿山、农业机械的堆焊与修补。
熔敷金属化学成分（％）（保护气体:CO2）
项目 C Cr Mo
保证值 ≤0.50 ≤3.00 ≤1.50
堆焊层硬度：HRC≥30
参考电流（DC+）
焊丝规格（mm） 焊接电流（A） 焊接电压（V）
φ1.2
φ1.4
φ1.6 220 26
注意事项:
1.施焊工件应做除油、除锈处理。
2.焊接时，气体流量一般在20～25L/min。
3.药芯焊丝焊接时，干伸长度应为15～25mm。
4.在堆焊大型工件前应适当预热至300℃左右。
5.焊丝库房的湿度应保持在小于60% 。
6.非真空包装焊丝存放时间不宜超过半年，真空包装焊丝存放时间不宜超过一年。

YD798耐磨焊丝YD798药芯焊丝详细介绍：

气体保护焊堆焊焊丝Gas ShieldedHardfacing Wires

牌号
Trade Name
直径
Diameter
HRC
（国家标准台式硬度计）
特点及主要用途
characteristicsandapplication
HB-YD114(Q)
1.6
50-55
(受强烈冲击后
After high impact)
高锰钢堆焊焊丝，受强烈冲击后，表面具有加工硬度的特点。
High-manganese steelhardfacing flux-cored wires, and applied to repair surface of high impact wear parts, cladding layer is impacted with work hardening.
HB-YD115(Q)
1.6
50-55
(受强烈冲击后After high impact)
用于受严重冲击高锰钢堆焊，加工硬化效果显著。
Applied to repair surface of high impact wear parts, cladding layer is impacted with work hardening.
HB-YD165(Q)
1.6
60-65
高硬度耐磨焊丝，适用于磨粒磨损表面堆焊
High hardness wear-resistant wire, it is used to abrasive wearsurfacing welding.
HB-YD172(Q)
1.6
≥40
用于堆焊齿轮、挖泥斗、矿山机械等磨损件
Applied to repair surface of high impact wear parts, such as gear aud bucket and mining machinery.
HB-YD207(Q)
1.6
≥50
用于堆焊推土机刀片，螺旋桨等磨损零件
Applied to repair surface of high wear parts, such as bulldozer blade and propeller.
HB-YD212(Q)
1.2/1.6
≥50
用于堆焊各种受磨损的机件表面，如齿轮、挖斗、矿山机械
Applied to repair surface of wear parts, such as gear mud bucket and mining machinery.
HB-YD256(Q)
1.6
HB≥170
高锰钢堆焊，适用于破碎机等受冲击磨损部位的堆焊
High-manganese steelhardfacing flux-cored Wires,it is applied to repair surface of high impact wear parts, such as Crusher.
HB-YD258(Q)
1.6
55-60
用于耐磨表面堆焊
Applied to repair surface of wear parts.
HB-YD265(Q)
1.6
60-65
高硬度耐磨焊丝，适用于磨粒磨损表面堆焊
High hardness wear-resistant wire, it is used to abrasive wearsurfacing welding.
HB-YD322(Q)
1.6
≥55
用于堆焊各种冲模及切削刃具，兼用于修复要求耐磨损性能较高之机械零件
Applied to repair surface ofhigh wear resistanceparts, such as die and cuttingcutlery.
HB-YD327A(Q)
1.6
≥55
专门用于模具堆焊，耐磨性能高于D322
Used tomouldsurfacing, wear resistance is better than D322.
HB-YD337(Q)
1.6
≥48
用于铸钢或锻钢上堆焊锻模
Applied to repairfo r g ing dieatcast steelorfo r g ing steel.
HB-YD397(Q)
1.6
≥40
用于堆焊铸钢或锻钢做坯体的热锻模或堆焊高强度耐磨件
Applied to repair hotfo r g ing dieatcast steelor fo r g ing steel, or highstrengthwear surfacing.
HB-YD405A(Q)
1.6
50-59
用于热轧辊开坯辊堆焊
Applied to repair hot-rolling blooming rollor.
HB-YD430A(Q)
1.6
20-35
打底层堆焊焊丝
A backing hardfacing flux-cored Wires
HB-YD488A(Q)
1.6
45-50
用于轧辊堆焊
Applied to repair rollor
HB-YD507Mo(Q)
1.6
35-45
用于510℃以下中高压阀门堆焊
Applied to valve which operating temperature is less than 510℃.
HB-YD518(Q)
1.6
40-50
用于连铸辊堆焊
Applied to repaircontinuous caster roller
HB-YD688(Q)
1.6
50-60
用于磨煤辊打底焊(韧性好，可以多层堆焊)
Used to coal roller backing welding.
HB-YD788(Q)
1.6
55-62
硬度高，可以多层堆焊。
High hardness andmulti-layer welding
HB-YD888(Q)
1.2, 1.6
60-65
硬度高，堆焊层厚度不超过6mm。
High hardness, but thethicknessofsurfacing layeris less than 6mm.
HB-YD888Ni(Q)
1.2
58-65
高铬合金焊丝，用于耐磨表面堆焊
Applied to repair surface of wear parts.
HB-YD988(Q)
1.6
55-63
高铬合金焊丝，用于耐磨表面堆焊
Applied to repair surface of wear parts.
HB-YD990(Q)
1.6
55-65
用于高温耐磨堆焊。
Applied to repair surface ofhigh temperaturewear parts.
HB-YD58(Q)
1.6
55-60
高温耐磨焊丝，用于化推焦机磨靴的堆焊。
high temperaturewear hardfacing wires,
HB-YD67(Q)
1.6
58-63
用于耐磨表面堆焊
Applied to repair surface of wear parts.
HB-YD95(Q)
1.6
55-63
高铬合金焊丝，用于耐磨表面堆焊
Applied to repair surface of wear parts.
HB-DG7(Q)
1.6
52-60
地铁盾构施工刀具刃口堆焊专用，也可用于煤碳石装载机料斗和刃口堆焊修复。
Applied to repair surface of high impact wear parts, such as shiled machine, excavator bucket and hopper of mining machinery products.