EXTEM VH1003M Resin SABIC Innovative Plastics Asia Pacific PEI，
EXTEM? VH1003M resin
聚醚酰亚胺
SABIC Innovative Plastics Asia Pacific
SABIC EXTEM? VH1003M TPI
透明热塑性聚酰亚胺（TPI）树脂，玻璃化转变温度（TG）为247C。该产品具有薄壁FR功能，并具有UL94V0列表。根据VDE/DIN472第815部分，该材料符合RoHS标准，且无卤素。
产品说明：
Transparent, Thermoplastic Polyimide (TPI) resin with a glass transition temperature (Tg) of 247C. Internal mold release. This product has thinwall FR capability and has a UL94 V0 listing. This material is RoHS compliant and also halogen free according VDE/DIN 472 part 815. Resin is a Dual-use item and is subject to export control restrictions under both U.S. 15 CFR 774 and Annex I of Reg. (EC) 428/2009 as ECCN 1C008. Diversion contrary to law is prohibited.
添加剂：脱模
特性：无卤，阻燃性
用途：薄壁部件
机构评级：DIN VDE 0472 第815部分
RoHS 合规
外观：清晰/透明
加工方法：注射成型
EXTEM? VH1003M resin 物性表
|
物理性能 |
额定值 |
单位制 |
测试方法 |
|
比重 |
1.30 |
g/cm3 |
ASTM D792, ISO 1183 |
|
熔流率（熔体流动速率）(367°C/6.6 kg) |
16 |
g/10 min |
ASTM D1238 |
|
溶化体积流率（MVR）(360°C/5.0 kg) |
8.50 |
cm3/10min |
ISO 1133 |
|
收缩率 |
|
|
内部方法 |
|
流动 1 |
0.50 到 0.70 |
% |
内部方法 |
|
流动 : 3.20 mm |
0.50 到 0.70 |
% |
内部方法 |
|
横向流动 : 3.20 mm |
0.50 到 0.70 |
% |
内部方法 |
|
吸水率 |
|
|
ISO 62 |
|
饱和, 23°C |
1.8 |
% |
ISO 62 |
|
平衡, 23°C, 50% RH |
0.65 |
% |
ISO 62 |
|
热性能 |
额定值 |
单位制 |
测试方法 |
|
载荷下热变形温度 |
|
|
|
|
0.45 MPa, 未退火, 6.40 mm |
237 |
°C |
ASTM D648 |
|
1.8 MPa, 未退火, 3.20 mm |
217 |
°C |
ASTM D648 |
|
1.8 MPa, 未退火, 6.40 mm |
230 |
°C |
ASTM D648 |
|
1.8 MPa, 未退火, 64.0 mm 跨距 16 |
228 |
°C |
ISO 75-2/Af |
|
维卡软化温度 |
|
|
|
|
-- |
242 |
°C |
ASTM D1525, ISO 306/B50 1217 |
|
可燃性 |
额定值 |
单位制 |
测试方法 |
|
灼热丝易燃指数 (3.20 mm) |
960 |
°C |
IEC 60695-2-12 |
|
热灯丝点火温度 (3.00 mm) |
850 |
°C |
IEC 60695-2-13 |
|
极限氧指数 |
45 |
% |
ISO 4589-2 |